Corrosion Behavior of 2205 Duplex Stainless Steel

Jiangsu Sheye Metal Co.,Ltd | Updated: Dec 19, 2016
Source: SheyeMetal

   The corrosion behavior of 2205 duplex stainless steel was compared with that of AISI type 316L stainless steel. The 2205 stainless steel is a potential orthodontic bracket material with low nickel content (4 to 6 wt%), whereas the 316L stainless steel (nickel content: 10 to 14 wt%) is a currently used bracket material.

      Our findings indicate that (1) 2205 stainless steel exhibits better corrosion resistance than 316L stainless steel; (2) when 2205 is coupled with a less corrosion resistant material (316L stainless steel), 2205 stainless steel shows decreases corrosion; and (3) this trend is reduced when the exposed surface areas have a anodic / cathodic ratio less than 1 and that 2205, unlike 316L, is not subject to crevice corrosion.

      From the standpoint of corrosion resistance, the use of 2205 as an orthodontic bracket material seems to be justified when the arch wire material is stainless steel or titanium. Use of this alloy could decrease the amount of corrosion products to which a patient would be exposed that could minimize nickel allergy problems potentially associated with orthodontic treatment.


Product Categories

Fast Track

  • Feedback
    Jiangsu Sheye Metal Co.,Ltd welcomes your comments! Please fill this form to give us feedback or report any problem when experiencing our website.
  • Quick Navigation
  • Contact Us
    Address: #2201, Block B, WTC (World Trade Center), Wujin District, Changzhou
    Tel: +86-519-89885505    
    Fax: +86-519-81188671    
    E-mail: sales@syemetal.com
Copyright © Jiangsu Sheye Metal Co.,Ltd